ARBOFLEX® PU Product Application
ARBOFLEX® PU is brush or roller applied and for best results should be applied to the following surfaces:
Roofing - Flat and low pitched roofs, balconies and overhangs
Flooring - Walkable floors with waterproofing and anti slip finish
Structural concrete slabs, and concrete walls and foundations
Metal and asbestos roofs
Swimming pools, artificial lakes and ponds
Green roof compatible
On inverted roofs
The Benefits of ARBOFLEX® PU
ARBOFLEX® PU offers seamless finishing, green roof compatibility and has a fast and easy installation process. Alongside these benefits, it’s also:
Instantly water-resistant
Ready to use straight out of the tin – single component PU
Weather-resistant: can be used all year round
BBA Certified
Adapts to any surface such as uneven, curved or irregular surfaces
ARBOFLEX® PU Product Range
ARBOFLEX® PU MATTING
ARBOFLEX® 225 gsm Matt is specially designed to increase adhesion and strength of continuous waterproofing membranes even on concrete or mortar substrates with residual moisture. The matting also reinforces the liquid membrane at detail work or critical points & areas.
PRODUCT APPLICATION
To be used in all field areas.
To reinforce details such as upstands, internal outlets, fissures, expansion joints, active cracks, and insulation joints.
Reinforced expansion joints, active cracks, insulation joints.
It strengthens the bond between different materials & expansion joints.
Available in 20m & 60m rolls. Roll width 1m.
ARBOFLEX® PU PRIMER
ARBOFLEX PU PRIMER is a single component, low viscosity, high solids content polyurethane resin. It has been specifically designed to increase bonding and improve the surface levelling of the substrates prior to the application of ARBOFLEX PU.
Specifically designed to increase the adherence
Apply on porous substrates such as concrete, mortar, or on plywood.
Available in 5L tins
ARBOFLEX® PU THICKENER
ARBOFLEX® PU THICKENER is a polymeric thickener, developed specifically as a liquid additive for the polyurethane liquid membrane ARBOFLEX® PU to prevent sagging while drying. For use on vertical or sloped surfaces, providing thixotropic properties.
In order to achieve the desired proportion, mix 800 ml of thickener per 20 kg of ARBOFLEX PU.
Available in a 1L can.
ARBOFLEX® PU ACCELERATOR
Single coat additive to apply over ARBOFLEX® PU membrane to facilitate its physical and mechanical properties. It can accelerate drying time even in low temperatures.
KEY BENEFITS
Fast installation time
Eliminates defects and formation of air bubbles
Reduces drying and curing times on polyurethane, especially in winters, cold weather & in low humidity
Improves & increases the mechanical properties of ARBOFLEX® PU
Available in 2L & 500ml tins.
ARBOFLEX® PU TOP COAT
ARBOFLEX® PU Top Coat is a single-component aliphatic resin for treatment and protection against UV rays. It forms a flexible, seamless layer in a satin finish, with excellent adhesion and mechanical properties. It forms a resistance to abrasion and stress, weathering, temperature variations, UV radiation. As a continuous film with excellent adhesion and mechanical properties, it is resistant to abrasion, stress, weathering, extreme temperatures and UV radiation.
Available in 5 Kg tins.
ARBOFLEX® PU SA PRIMER
SA is a solvent free, one part elastomeric sealant adhesive based on neutral curing silicone polymer technology.
ARBOFLEX® Liquid Carrier Membrane
ARBOFLEX® Liquid Carrier Membrane is a polyester-reinforced roofing base layer, saturated and coated with high-quality SBS (Styrene-Butadiene-Styrene) modified bitumen. The membrane is protected with fine grained sand on its upper layer, whilst the bottom layer features a self-adhesive compound coating, covered with removable film. It is specifically designed to act as a carrier membrane when used with ARBOFLEX®PU liquid waterproofing. The product is intended to be a part of a multi-layer built-up roofing system.
Roll size: 15m long with 1m wide
Technical Information
Properties | Value | |
---|---|---|
Dry Time | +1.5mm | |
Weight per unit area | ± 5~6 hours approx | |
Elongation at 23ºC | >600% | |
Tensile strength at 23ºC | 2~3 MPa | |
Application method | Brush or roller applied | |
Application system | ± 2~3 thin layers by roll or brush to achieve the recommended thickness |